前言：1302UV-08 PC 韩国LG 耐老化
产品物性表
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTMD792 | 1.20 | g/cm? | |
| 熔流率（熔体流动速率）(300°C/1.2kg) | ASTMD1238 | 8.0 | g/10min | ||
| 收缩率-流动 | ASTMD955 | 0.50到0.70 | % | ||
| 吸水率 | 23°C,24hr | ASTMD570 | 0.15 | % | |
| 平衡,23°C,50%RH | ASTMD570 | 0.32 | % | ||
| 硬度 | 洛氏硬度 | M级 | ASTMD785 | 73 | |
| R级 | ASTMD785 | 118 | |||
| 机械性能 | 拉伸模量 | ASTMD638 | 2410 | MPa | |
| 抗张强度 | 屈服 | ASTMD638 | 60.0 | MPa | |
| 断裂 | ASTMD638 | 72.0 | MPa | ||
| 伸长率 | 屈服 | ASTMD638 | 6.0 | % | |
| 断裂 | ASTMD638 | 150 | % | ||
| 弯曲模量 | ASTMD790 | 2410 | MPa | ||
| 弯曲强度 | ASTMD790 | 96.0 | MPa | ||
| 耗性-ChangeinHaze1 | ASTMD1004 | 45 | % | ||
| 冲击性能 | 悬壁梁缺口冲击强度2(23°C,3.20mm) | ASTMD256 | 900 | J/m | |
| 无缺口悬臂梁冲击(23°C) | ASTMD256 | 无断裂 | |||
| 装有测量仪表的落镖冲击3(23°C,3.20mm,TotalEnergy) | ASTMD3763 | 89.0 | J | ||
| 热性能 | 载荷下热变形温度 | 0.45MPa,退火,4.00mm | ASTMD648 | 144 | °C |
| 1.8MPa,未退火,4.00mm | ASTMD648 | 128 | °C | ||
| 1.8MPa,退火,4.00mm | ASTMD648 | 141 | °C | ||